Gallium arsenide (GaAs) was once the automatic choice of semiconductor material for high-frequency solid-state devices, components, and integrated circuits (ICs), from amplifiers to switches.

As GaAs devices grew in popularity for RF/microwave applications, they rapidly replaced legacy silicon-based semiconductors, such as bipolar transistors and metal-oxide-semiconductor field-effect transistors (MOSFETs), which were limited in frequency compared to GaAs field-effect transistors (FETs), heterojunction bipolar transistors (HBTs), and high electron mobility transistors (HEMTs).

During the last decade, however, gallium nitride (GaN) has become the favorite high-frequency semiconductor compound, steadily replacing GaAs in many RF/microwave applications, especially where higher-frequency, higher-power semiconductors are required. But why the steady shift to GaN and just how different in performance are GaAs and GaN?

GaN and GaAs are both compound semiconductor materials, each composed of two elements. The materials are grown in the form of ingots, which are cut into thin wafers (see figure) upon which semiconductor devices, including passive circuit elements, are fabricated. GaAs is the more mature material and is commercially available in the form of wafers as large as 6 in. in diameter while GaN, which has been used to fabricate light-emitting diodes (LEDs) since the 1990s, is typically available in wafers as large as 2 in. in diameter.​

Mwrf Com Sites Mwrf com Files Uploads 2016 07 08 Pullquote Test 1

GaAs is well established as a substrate of choice for high-frequency, small-signal semiconductor devices, especially where low noise figure is needed, as in receiver front ends. GaAs monolithic microwave integrated circuits (MMICs) are widely used in portable wireless products, such as smartphones, tablets, and Wi-Fi devices. Components such as switches and amplifiers are typically incorporated into these GaAs MMICs, which are designed for operation at low voltages and currents typically available from a battery.

GaN, on the other hand, has come to be known as a power process, capable of fabricating active devices for amplifiers that can operate at voltages of +48 V dc and higher. With the higher-voltage capabilities of GaN devices and MMICs, they have become the active components of choice for such applications as power amplifiers in wireless base stations and have been steadily replacing high-frequency electron vacuum tubes in military radar and even in commercial and industrial microwave ovens. For a comparable output-power rating, GaAs amplifiers tend to be more linear, with less distortion, than GaN amplifiers, although GaN devices have been used with digital predistortion (DPD) to achieve enhanced linearity at higher frequencies.

Before attempting to compare differences in devices fabricated on the two high-frequency semiconductor materials, however, it is only necessary to assess the differences in characteristics of the two III-V compound semiconductors. These key material characteristics include relative dielectric constant (relative to the dielectric constant of a vacuum), breakdown voltage, electron mobility, saturation velocity, and thermal conductivity.

Mwrf Com Sites Mwrf com Files Uploads 2015 02 32 Jfig1 Web

GaN and GaAs are two of the semiconductor substrate materials used for high-frequency solid-state devices, fabricated on thin wafers. (Graphic courtesy of Xiamen Powerway Advanced Material Co., Ltd.)

GaN is considered a wide-bandgap material compared to GaAs, with a bandgap of about 3.4 eV for GaN compared to 1.4 eV for GaAs. A material’s bandgap related to the amount of energy required to shift an electron from the top of the valence band to the bottom of the conduction band within a semiconductor formed on that material. A wide bandgap typically refers to a material with bandgap of greater than 1 or 2 eV.

GaN typically exceeds GaAs in material parameters relating to higher energy and power, and in the speed of achieving higher-energy states. For example, the saturation velocity of GaN, at 2.7 × 107 cm/s, is somewhat higher than the 2.0 × 107 cm/s of GaAs. The critical breakdown voltage field determines the highest voltage that can be safely applied to a solid-state device, and the breakdown electric field of GaN, at 4 × 106 V/cm, is much higher than the 5 × 105 V/cm of GaAs.

GaN has certain traits that support smaller circuits for a given frequency and power level, allowing the higher power densities and efficiencies much sought after by designers of power-efficient wireless base stations and microcells. For one thing, the higher-voltage capacities of GaN allow the fabrication of much smaller devices for a given power level than on GaAs materials. For example, the defect density of any semiconductor wafer will limit the practical size of circuits that can be manufactured repeatably and reliably on that wafer, implying that device area be minimized for best production yields.

Because the power density of GaN materials is much higher than GaAs or even silicon semiconductor materials, thermal conductivity is an important material parameter for characterizing how well a device will dissipate heat due to dielectric and conductor losses as well as basic device inefficiencies. The thermal conductivity of GaN, at 1.7 W/cm-K, is more than three times the thermal conductivity of GaAs, at 0.46 W/cm-K. High thermal conductivity translates into the lowest temperature rise at conduction, a characteristic that enables GaN devices to handle higher power levels than GaAs devices using the same device structure, such as a field-effect transistor (FET).

GaN devices are currently fabricated on different substrate materials, such as GaN on silicon (Si) and GaN on silicon carbide (SiC) wafers, with some debate about which process offers the best performance. Some larger companies, such as Raytheon Co., maintain both GaAs and GaN foundries as part of their in-house capabilities in support of military applications. Many commercial foundries will offer details on the benefits of each process with some foundries, including WIN Semiconductors Corp., Global Communication Semiconductors LLC, and Qorvo, offering different forms of GaN processes along with GaAs fabrication services as well.

For those wishing a finer-grained comparison of GaN and GaAs materials, MACOM, with products based on more than a half-dozen semiconductor processes, offers a detailed comparison of the different semiconductor materials on their website.

Looking for parts? Go to SourceESB.

Summary
Gallium arsenide (GaAs) was once the preferred semiconductor material for high-frequency devices, but gallium nitride (GaN) has become more popular due to its higher power capabilities. GaAs is known for low noise and is used in portable wireless products, while GaN is favored for high-power applications like wireless base stations. GaN has a wider bandgap, higher energy parameters, and better thermal conductivity than GaAs. GaN devices are smaller and more efficient, with higher power densities. GaN can handle higher power levels due to its superior thermal conductivity. GaN devices are fabricated on various substrates like silicon and silicon carbide wafers. Companies like Raytheon Co. have both GaAs and GaN foundries for military applications. Commercial foundries like WIN Semiconductors Corp., Global Communication Semiconductors LLC, and Qorvo offer GaN and GaAs fabrication services. MACOM provides a detailed comparison of GaN and GaAs materials on their website.